| Feature | Grand ML™ Multilayered Zirconia | 
| Product Type | 3 layered Unstained, highly translucent zirconia for veneered restorations | 
| Translucency | Approximately 43% | 
| Strength | 1290 MPa | 
| Layers | Not specified | 
| Indications | Full contour crowns, multi-pontic bridge frames, inlay bridges, Maryland bridges, primary telescopes | 
| Shades Available | 16 shades (A1, A2, A3, A3.5, A4, B1, B2, B3, B4, C1, C2, C3, C4, D2, D3, D4) | 
| Sintering Temperature | 1400–1580°C (recommended 1530°C) | 
| Sintering Density | 6.07 ± 0.01 g/cm³ | 
| Coefficient of Thermal Expansion (CTE) | 10.5 ± 1.0 x 10⁻⁶ K⁻¹ (25–500°C) | 
| Composition | ZrO₂ + HfO₂ + Y₂O₃ ≥ 99%; Y₂O₃ 4.5–6%; Al₂O₃ ≤ 0.5%; other oxides ≤ 0.5% | 
| Health Canada Licensed | Yes | 
| Medical Device Class | IIa | 
Zirconia Multi Layered Pre-shaded Blanks are used for dental restoration using different Milling CAD/CAM System, diameter 98mm
Unstained, highly translucent, made of yttrium oxide stabilized, tetragonal ZrO₂. For the fabrication of fully and partially veneered frame constructions with high strength. Medical device Class IIa.
| CTE 10.5 ± 1.0 x 10⁻⁶K⁻¹ (25-500 °C) | 
| Density after sintering 6.07 ± 0.01 g/cm³ | 
| Bending strength (3-point bending test) > 1290 MPa | 
| Sintering temperature 1400-1580 °C | 
| Recommended 1530 °C | 
| Translucency 43% | 
Available in Sizes:
Available in Colors:
Free Shipping on all orders over $150 in Ontario and Quebec. Free Shipping at the rest of the provinces on all orders over $300. (Excluding Extra Heavy items)
Learn more here
Discover exocad globally renowned software solution for outstanding dental restoration designs – powered by passion, executed in excellence
High-performance, user-friendly open software solution for your implant planning and surgical guide design
 
         
       
                      
                   
                      
                   
                      
                   
                      
                   
                      
                   
                      
                   
            
           
           
            
           
            
           
           
            
           
           
            
           
           
            
          